高温変形中のLPSOマグネシウム合金の動的再結晶挙動【Powered by NICT】

Dynamic recrystallization behavior of magnesium alloys with LPSO during hot deformation

著者 (6件)： Yu Jianmin (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China) ,  Zhang Zhimin (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China) ,  Wang Qiang (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China) ,  Yin Xueyan (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China) ,  Cui Jinyu (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China) ,  Qi Hongna (College of Materials Science and Engineering, North University of China, 3 Xueyuan Road, Taiyuan 030051, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 704  ページ： 382-389  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 均質化処理のままMg12Gd,4-0.5Y2Zn10-0.4Zr合金の熱間変形と動的再結晶挙動を本論文で圧縮試験により調べた。本研究では,適切な変形域を提示した。異なる歪速度と温度下での合金の発生した不連続な動的再結晶の異なる程度。高温変形中のこれらの合金の臨界歪予測モデルは,加工硬化率θの計算,l nθ-ε曲線における変曲点と-(∂(l n θ)/∂ε)-ε曲線の最小値を得た。低歪速度と温度では,キンクバンド変形の結果は均一なひずみ生成に必須である機構を構成している。歪速度が増加すると,キンクバンド変形が有意に重篤な,新しいキンクはキンクバンド内に形成された,結晶粒微細化をもたらした。添加では,少量の不連続な動的再結晶が生じた。歪速度が増加すると,不連続な動的再結晶の体積分率は増加したが,キンクバンド変形は減少した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  体積率 ,  *マグネシウム合金 ,  キンクバンド ,  圧縮試験 ,  ジルコニウム合金 ,  予測モデル ,  *動的再結晶 ,  キンク ,  歪速度 ,  結晶粒微細化 ,  不連続性 ,  *高温変形
準シソーラス用語： 加工硬化率 ,  均質化処理 , 【Automatic Indexing@JST】

著者キーワード (4件)： Mg-Gd-Y-Zn-Zr合金 ,  動的再結晶 ,  臨界歪 ,  キンクバンド

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： 高温変形 ,  マグネシウム合金 ,  動的再結晶 ,  挙動