親電荷移動ギャップと銅酸塩における最大転移温度【Powered by NICT】

Relationship between the parent charge transfer gap and maximum transition temperature in cuprates

著者 (13件)： Ruan Wei (Department of Physics, Tsinghua University) ,  Hu Cheng (Institute of Physics, Chinese Academy of Sciences) ,  Zhao Jianfa (Institute of Physics, Chinese Academy of Sciences) ,  Cai Peng (Department of Physics, Tsinghua University) ,  Peng Yingying (Institute of Physics, Chinese Academy of Sciences) ,  Ye Cun (Department of Physics, Tsinghua University) ,  Yu Runze (Institute of Physics, Chinese Academy of Sciences) ,  Li Xintong (Department of Physics, Tsinghua University) ,  Hao Zhenqi (Department of Physics, Tsinghua University) ,  Jin Changqing (Institute of Physics, Chinese Academy of Sciences) ,  Zhou Xingjiang (Institute of Physics, Chinese Academy of Sciences) ,  Weng Zhengyu (Collaborative Innovation Center of Quantum Matter) ,  Wang Yayu (Department of Physics, Tsinghua University)
資料名： Kexue Tongbao  (Kexue Tongbao)
巻： 61  号： 23  ページ： 1826-1832  発行年： 2016年 
JST資料番号： C2862A  ISSN： 2095-9273  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 銅酸化物高温超伝導体に関する最大パズルの一つは最大転移温度(T(c,max)),種々の化合物で30未満から130K以上に変化することを決定するものである。この劇的な変化にもかかわらず,ロバストな傾向は,各ファミリー内で,二重層化合物は常に単層よりも高いT(c,max)を持つことである。ここでは,走査型トンネル顕微鏡を用いて二種の異なるファミリに属する四銅酸化物の親化合物の電子構造を調べた。各ファミリー内で,二重層状化合物は非常に小さい電荷移動ギャップサイズ((CT)),(CT)とT(C,max)の間の明確な逆相関を示すことが分かった。これらの結果は,電荷移動ギャップは銅酸化物の超伝導物理学,ドープMott絶縁体の観点から高T_c機構に重要な新たな光を当てるで重要な役割を果たすことを示唆する。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 層状化合物 ,  高温超伝導体 ,  走査型トンネル顕微鏡 ,  *転移温度 ,  超伝導 ,  ロバスト性 ,  電子構造 ,  酸化銅 ,  ドーピング ,  *電荷移動 ,  Mott-Hubbard絶縁体 ,  二重層 ,  *銅酸塩
準シソーラス用語： 逆相関 ,  パズル , 【Automatic Indexing@JST】

著者キーワード (5件)： Cuprates ,  Mott絶縁体 ,  電荷移動ギャップ ,  最大転移温度 ,  走査型トンネル顕微鏡法

分類 (3件)： 電子顕微鏡,イオン顕微鏡  (BD02050B) ,  炭素とその化合物  (YB02060D) ,  固体デバイス製造技術一般  (NC03030V)

タイトルに関連する用語 (4件)： 電荷移動 ,  ギャップ ,  銅酸塩 ,  転移温度