Ni-Cr-W基超合金の結晶粒界における元素偏析と相析出挙動【Powered by NICT】

Elements segregation and phase precipitation behavior at grain boundary in a Ni-Cr-W based superalloy

著者 (5件)： Dong Ruifeng (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, PR China) ,  Li Jinshan (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, PR China) ,  Zhang Tiebang (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, PR China) ,  Hu Rui (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, PR China) ,  Kou Hongchao (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, PR China)
資料名： Materials Characterization  (Materials Characterization)
巻： 122  ページ： 189-196  発行年： 2016年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,結晶粒界(GB)炭化物とGB偏析は,GB特性に基づいて調べた。M_23C_6型炭化物が支配的なGB炭化物であることが分かった。GB M_23C_6の炭化物は,一般高傾角粒界(HAGBs)に析出することを好むが,低い界面エネルギーを持つΣ3コヒーレント双晶境界は一般的にM_23C_6を沈殿させるために影響を受けなかった。これに対応して,明瞭な偏析が一般的なHAGBで観測され,非自明偏析はΣ3コヒーレント双晶境界で検出された。GB M_23C_6とγマトリックス間のGB偏析と方位関係(OR)と組み合わせて,GB M_23C_6の析出機構を提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 炭化物 ,  双晶境界 ,  超合金 ,  高傾角粒界 ,  *結晶粒界 ,  表面エネルギー ,  *偏析 ,  コヒーレンス

著者キーワード (4件)： Ni基超合金 ,  粒界 ,  元素偏析 ,  炭化物析出

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (8件)： Ni ,  Cr ,  超合金 ,  結晶粒界 ,  元素 ,  偏析 ,  析出 ,  挙動