TiO_2/XLPEナノ複合材料の誘電特性に関する研究【Powered by NICT】

Study on dielectric properties of TiO₂/XLPE nanocomposites

著者 (5件)： Wang Youyuan (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China) ,  Xiao Kun (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China) ,  Wang Can (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China) ,  Yang Lijun (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China) ,  Wang Feipeng (State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China)
資料名： IEEE Conference Proceedings  (IEEE Conference Proceedings)
巻： 2016  号： ICHVE  ページ： 1-4  発行年： 2016年 
JST資料番号： W2441A  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： TiO_2/XLPEナノ複合材料の誘電特性に焦点を当て,TiO_2ナノ粒子を,種々の質量濃度(1wt%,3wt%,および5wt%)を有するXLPEマトリックスに添加した。TiO_2/XLPEナノ複合材料の体積抵抗率はXLPE,充填濃度とともに増加したよりも高いことが分かった。さらに,TiO_2/XLPEナノ複合材料は,低い誘電率と低い誘電損失,充填濃度と共に増加し,測定周波数の減少を有していた。パルス電気音響(PEA)測定の結果は,全空間電荷が抑制され,電荷はTiO_2/XLPEナノ複合材料において消失し,試料の中央に少量の負電荷を残すことを示した。本論文における分析によると,新しい界面領域はTiO_2ナノ粒子を充填のために多くの深いトラップ,「孤立波」移動の有効距離を短縮し,キャリア移動度を大幅に低減できるを導入した。一方,低キャリア移動度は再結合過程を増強し,不純物のイオン化過程を弱め,TiO_2/XLPE中のヘテロ電荷の消失をもたらした。さらに,界面逆電場は電極からの電荷注入を抑制するばかりでなく,マトリックスの中の電場を強化し,蓄積された空間電荷は,タイムリーな材料から移動できるようにした。Copyright 2017 The Institute of Electrical and Electronics Engineers, Inc. All Rights reserved. Translated from English into Japanese by JST【Powered by NICT】

シソーラス用語： 電気音響 ,  電場 ,  界面 ,  誘電損失 ,  *ナノ複合材料 ,  空間電荷 ,  *XLPE ,  キャリア注入 ,  周波数 ,  *誘電性 ,  不純物 ,  電荷 ,  ナノ粒子 ,  誘電率 ,  キャリア移動度

分類 (1件)： 絶縁材料  (NA04030W)

タイトルに関連する用語 (4件)： XLPE ,  ナノ複合材料 ,  誘電特性 ,  研究