電気化学堆積によるアルミナ内のCo_1-xSn_x(x=0.3-0.7)ナノワイヤ合金の構造と磁性に及ぼす電圧変動の影響

Influence of voltage variation on structure and magnetic properties of Co_1-xSn_x (X = 0.3-0.7) nanowire alloys in alumina by electrochemical deposition

著者 (10件)： AHMAD Naeem (International Islamic Univ., Islamabad, PAK) ,  AHMAD Naeem (Inst. of Physics, Chinese Acad. of Sci. (CAS), Beijing, CHN) ,  KHAN Suleman (International Islamic Univ., Islamabad, PAK) ,  LIAQAT M. Arman (International Islamic Univ., Islamabad, PAK) ,  AWAIS Muhammad (International Islamic Univ., Islamabad, PAK) ,  SHAH Saqlain A. (Forman Christian Coll. (Univ.), Lahore, PAK) ,  AHMED Ishfaq (International Islamic Univ., Islamabad, PAK) ,  JABEEN Nyla (International Islamic Univ., Islamabad, PAK) ,  MAJID Abdul (Univ. Gujrat, Gujrat, PAK) ,  IQBAL Javed (Quaid-i-azam Univ., Islamabad, PAK)
資料名： Applied Physics. A. Materials Science & Processing  (Applied Physics. A. Materials Science & Processing)
巻： 123  号： 1  ページ： 65,1-7  発行年： 2017年01月 
JST資料番号： D0256C  ISSN： 0947-8396  CODEN： APHYCC  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 陽極酸化アルミニウム(AAO)テンプレート中に交流(AC)電着によってCo_1-xSn_x(x=0.3-0.7)ナノワイヤを高密度かつ均一サイズで作製した。AAOテンプレートはナノ多孔性でそのフィーチャは陽極酸化溶液,温度,電圧又は電流密度によって制御できる。得られたナノワイヤの長さは1μm,直径は170nmであった。このナノワイヤの構造は若干の異相を含む六方晶系であった。結晶粒径はAC電圧と共に増加した。このナノワイヤのヒステリシス曲線は異なる等方的で強磁性的挙動を示す。AC電圧を次第にあげて行くと,磁性イオンの堆積が減少し,その結果抗磁力(H_C)と飽和磁化(M_S)が減少する。電圧が臨界値(11-13V)を越えると磁気ドメインは分解し,欠陥クラスタとナノ構造アイランドが形成される。その結果としてH_CとM_Sは増加に転ずる。H_Cの非線型的電圧依存性はより多くの磁性イオンの置換とドメイン壁のピン止めによって説明できる。

シソーラス用語： *コバルト合金 ,  スズ含有合金 ,  *ナノワイヤ ,  酸化アルミニウム ,  *電着 ,  結晶構造 ,  磁性薄膜 ,  *強磁性 ,  *保磁力 ,  *飽和磁化 ,  鋳型効果 ,  細孔径分布 ,  *アルミナ ,  *アノード酸化 ,  *多孔質体 ,  陽極酸化アルミニウム
準シソーラス用語： 電気化学堆積

分類 (4件)： 金属薄膜  (BK14030T) ,  化成処理  (WC08050J) ,  金属の磁区及び磁化過程  (BM06112D) ,  磁性材料  (NA04040H)

タイトルに関連する用語 (6件)： 電気化学堆積 ,  アルミナ ,  ナノワイヤ ,  合金 ,  磁性 ,  電圧変動