凝固中の亜共晶Te In合金中に形成される平衡相の微細構造と組成【Powered by NICT】

The microstructure and composition of equilibrium phases formed in hypoeutectic Te-In alloy during solidification

著者 (5件)： Wang Baoguang (Department of Materials Physics and Chemistry, University of Science and Technology Beijing, Beijing 100083, China) ,  Hu Jinwu (Center of Failure Analysis, Central Iron and Steel Research Institute, Beijing 100081, China) ,  Wang Chongyun (Department of Materials Physics and Chemistry, University of Science and Technology Beijing, Beijing 100083, China) ,  Yang Wenhui (Department of Materials Physics and Chemistry, University of Science and Technology Beijing, Beijing 100083, China) ,  Tian Wenhuai (Department of Materials Physics and Chemistry, University of Science and Technology Beijing, Beijing 100083, China)
資料名： Materials Characterization  (Materials Characterization)
巻： 125  ページ： 46-50  発行年： 2017年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 紫外検出光電陰極の重要なテルル原子蒸発源として,亜共晶Te_75In_25合金は約10~ 2の遅い凝固速度を用いて調製した。調製されたままの合金中に形成された平衡相の微細構造および化学組成を本研究で研究した。実験結果は,調製したままのTe In合金は一次In_2Te_5相と共晶In_2Te_5/Te相で構成されていたことを示した。共晶In_2Te_5/Te相は一次In_2Te_5相の結晶粒界に分布している。遅い凝固速度では,過度のインジウム溶質を含まない純粋な共晶Te相が得られ,共晶Te相のTe含有量が100mass%である。さらに,In_2Te_5とTe相の間の応力はTe_75In_25合金中のテルル蒸気圧を減少させるのに重要な役割を果たしていると考えられる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒界 ,  相平衡 ,  ミスフィット ,  *テルル ,  溶質 ,  微細構造 ,  凝固速度 ,  *インジウム ,  蒸気圧 ,  光電陰極 ,  *凝固 ,  化学組成 ,  *合金 ,  *インジウム合金 ,  *共晶

著者キーワード (4件)： Te In合金 ,  Microstructure ,  遅い凝固 ,  ミスフィット

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 凝固 ,  Te ,  In合金 ,  平衡相 ,  微細構造 ,  組成