Yu木Ju材の従来の乾燥基準の最適化に関する研究【JST・京大機械翻訳】

Optimization of conventional drying schedule of converted elm timber

著者 (5件)： Liang Xiaoman (MOE Key Laboratory of Wooden Material Science and Application, Beijing Key Laboratory of Wood Science and Engineerings, Beijing Forestry University) ,  Meng Fanyang (MOE Key Laboratory of Wooden Material Science and Application, Beijing Key Laboratory of Wood Science and Engineerings, Beijing Forestry University) ,  Gao Jianmin (MOE Key Laboratory of Wooden Material Science and Application, Beijing Key Laboratory of Wood Science and Engineerings, Beijing Forestry University) ,  Yu Naiqiu (Wood Conservation and Development Center) ,  Chen Yao (MOE Key Laboratory of Wooden Material Science and Application, Beijing Key Laboratory of Wood Science and Engineerings, Beijing Forestry University)
資料名： Anhui Nongye Daxue Xuebao  (Anhui Nongye Daxue Xuebao)
巻： 43  号： 5  ページ： 743-748  発行年： 2016年 
JST資料番号： C2002A  ISSN： 1672-352X  CODEN： ANDXB8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 属は乾燥することが難しく、乾燥の欠陥が発生しやすい。50MM厚さのYu木Ju材に対して、その乾燥過程に存在する問題に基づき、応力測定により中間処理の回数と時間を調整し、Yu木Ju材の通常の乾燥基準に対して最適化を行った。また,重量測定法を用いて,プローブの含水量を修正し,補正関数を得て,乾燥基準の正確な実施を保証した。その結果,最適化された乾燥基準に従って,乾燥重量は60.0%±3.0%から10.0%±1.0%に減少し,乾燥サイクルは626時間から506時間に短縮され,乾燥時間は節約されることを示した。乾燥後の材料の厚さにおける含水量の偏差と残留応力はそれぞれ46.73%と33.49%減少し、各項目の品質検査指標は基本的に国家一級基準に達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 重量測定 ,  *最適化 ,  プローブ ,  残留応力 ,  応力測定 ,  含水量 ,  品質検査 ,  乾物量
準シソーラス用語： 乾燥時間 , 【Automatic Indexing@JST】

著者キーワード (4件)： elm timber ,  drying schedule ,  drying schedule optimization ,  moisture content correction

分類 (4件)： 製材・加工  (FF05032S) ,  金属材料  (HC02020X) ,  材料試験  (HB02020U) ,  木材の性質・構造  (FF05020Z)

タイトルに関連する用語 (3件)： 木 ,  最適化 ,  研究