高炉スラグ混合セメントモルタルの圧縮強度混合物設計に及ぼす石灰石粉と石膏の影響

Effect of Limestone Powder and Gypsum on the Compressive Strength Mixture Design of Blast Furnace Slag Blended Cement Mortar

著者 (6件)： Kim Junho (Course of Advanced Sustainable and Environmental Engineering, Muroran Institute of Technology, Muroran, Japan.) ,  Na Seunghyun (Product Development Department, Nippon Steel & Sumikin Cement Co. Ltd., Muroran, Japan.) ,  Zhang Wenyan (Center of Environmental Science and Disaster Mitigation for Advanced Research, Muroran Institute of Technology, Muroran, Japan.) ,  Zhang Wenyan (School of Material Science and Engineering, Henan Polytechnic University, Jiaozuo, China.) ,  Sagawa Takahiro (Department of Civil Environmental Engineering, Maebashi Institute of Technology, Maebashi, Japan.) ,  Hama Yukio (College of Environmental Technology, Graduate School of Engineering, Muroran Institute of Technology, Muroran, Japan.)
資料名： Journal of Advanced Concrete Technology (Web)  (Journal of Advanced Concrete Technology (Web))
巻： 15  号： 2  ページ： 67-80(J-STAGE)  発行年： 2017年 
JST資料番号： U0424A  ISSN： 1347-3913  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 日本 (JPN)  言語： 英語 (EN)

抄録/ポイント： 本稿では,石灰石粉(LSP)及び石膏(CS)などの各種鉱物混和剤を配合した高炉スラグ(BFS)モルタル混合物の圧縮強度向上について検討した。BFS混合モルタル混合物の強度を改善するために,BFSの置換率は15,20,25重量%,LSPの置換率は2,3,4,5重量%,CSの置換率は2重量%とした。セメント,BFSと鉱物混和剤の使用から生じる水和反応と生成物を,XRD/Rietveld法で定量的に検討し,生成した水和物と強度との関係を調べた。実験的調査により,BFS15重量%,LSP4重量%およびCS2重量%を含むモルタル混合物が,通常のポルトランド・セメント・モルタル混合物と同様の圧縮強度を示すことが明らかになった。加えて,BFS置換率の増加とともに強度が減少することが判明した。BFS置換率が20重量%を超えると,LSPはBFSセメントの強度向上に影響を与え,CSはBFSセメントの初期強度の向上に影響を与えた。(翻訳著者抄録)

シソーラス用語： *セメントモルタル ,  *高炉スラグ ,  混和剤 ,  石灰石 ,  石膏 ,  添加物効果 ,  置換率 ,  水和反応 ,  *圧縮強さ ,  Rietveld法

分類 (1件)： モルタル,コンクリート  (RA06042H)

引用文献 (42件)：

• 1) Melo Neto, A. A. M, Cincotto, M. A. and Repette, W., (2010). “Mechanical properties, drying and autogenous shrinkage of blast furnace slag activated with hydrated lime and gypsum.” <i>Cement & Concrete Composites</i>, 32(4), 312-318.
• 2) Barnett, S. J., Soutsos, M. N., Millard, S. G. and Bungey, J. H., (2006). “Strength development of mortars containing ground granulated blast-furnace slag: Effect of curing temperature and determination of apparent activation energies.” Cement and Concrete Research, 36, 434-440.
• 3) Bonavetti, V. L., Rahhal, V. F. and Irassar, E. F., (2001). “Studies on the carboaluminate formation in limestone filler-blended cements.” Cement and Concrete Research, 31, 853-859.
• 4) Boukendakdji, O., Kadri, E. H. and Kenai, S., (2012). “Effects of granulated blast furnace slag and superplasticizer type on the fresh properties and compressive strength of self-compacting concrete.” <i>Cement & Concrete Composites</i>, 34, 583-590.
• 5) Castellano, C. C., Bonavetti, V. L., Donza, H. A. and Irassar, E. F., (2016). “The effect of w/b and temperature on the hydration and strength of blast furnace slag cements.” Construction and Building Materials, 11, 679-688.

タイトルに関連する用語 (9件)： 高炉スラグ ,  混合セメント ,  モルタル ,  圧縮強度 ,  混合物 ,  設計 ,  石灰 ,  石粉 ,  石膏